POLYLAC® PA-757 General Grade ABS CHIMEI

Home » POLYLAC® PA-757

Ari-arian	Paraan ng ISO	Kundisyon ng Pagsubok	Yunit	PA-757 Halaga
Index ng Melt Flow	1133	220℃×10KG	ml/10 min	18
Mass Density	1183	23 ℃	g / cm³	1.05
Mga Katangian ng Makunot
– Lakas ng Tensile (Yield)	527	50 mm / min	MPa	47
– Lakas ng Tensile (Break)	527	50 mm / min	MPa	34
– Pagpapahaba ng Tensile	527	50 mm / min	%	30
Flexural na Katangian
– Flexural na Lakas	178	2 mm / min	MPa	76
– Flexural Modulus	-	2 mm / min	GPa	2.2
Lakas ng epekto
– Izod (23℃ Notched)	180 / 1A	23 ℃	KJ/m²	19
– Izod (-30 ℃ Binaw)	180 / 1A	-30 ℃	KJ/m²	9
– Charpy (23 ℃ Binaw)	179	23 ℃	KJ/m²	21
– Charpy (-30 ℃ Binaw)	179	-30 ℃	KJ/m²	10
Katangiang thermal
– Vicat Softening Temp (1Kg)	306	50℃/oras	℃	104
– Vicat Softening Temp (5Kg)	306	50℃/oras	℃	100
– HDT (1.8 MPa Unannealed)	75 / A	1.8 MPa	℃	83
– HDT (1.8 MPa Annealed)	75 / A	1.8 MPa	℃	98
– Coefficient ng Thermal Expansion	11359	-	1/℃	8.6×10⁻⁵
Iba Pang Mga Katangian
- Pagkasunog	-	Ul-94	Marka	1.5mm HB
– Pag-urong ng amag	294-4	-	%	0.4-0.7
– Simbolo ng Materyal	1043	-	Pagtatalaga	> ABS

POLYLAC® PA-757