HDPE B1054 is specially designed for blow molding and jerry cans.
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190°C and 5 kg load | 0.45 | g/10 min |
| at 190°C and 21.6 kg load | 9.5 | g/10 min |
| Density at 23°C | 954 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| Tensile modulus | 1250 | MPa |
| Tensile Stress at Yield | 27 | MPa |
| Tensile Strain at Yield | 10 | % |
| Tensile Impact Strength at -30°C (Notched) | 90 | kJ/m² |
| Hardness (Shore D) | 62 | – |
| FNCT (3.5 MPa, 2 % Igepal BC/9, 80°C) | 40 | Hrs |
Sabic HDPE B4660 is suitable for Dairy products and Juice Packaging. They are primarily Designed for imparting high rigidity, toughness and good processability.
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| @ 190°C & 2.16 kg load | 0.7 | g/10 min |
| @ 190°C & 5 kg load | 2.8 | g/10 min |
| @ 190°C & 21.6 kg load | 46 | g/10 min |
| Density at 23°C | 961 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| 1% Secant Modulus | >1000 | MPa |
| Tensile Strength at Yield | 30 | MPa |
| Tensile Strength at Break | 18 | MPa |
| Tensile Elongation at Break | 500 | % |
| Flexural Strength | 28 | MPa |
| Flexural Modulus | 1100 | MPa |
| Izod Impact Strength | 150 | J/m |
| Hardness (Shore D) | 66 | – |
| THERMAL PROPERTIES | ||
| Vicat Softening Point | 127 | °C |
| Brittleness Temperature | <-75 | °C |
SABIC HDPE B5210 is typically used for blow molding of light weight UN certified cans from 2 to 20 liters.
| PROPERTIES | TYPICAL VALUES | UNITS |
| MECHANICAL PROPERTIES | ||
| Tensile test | ||
| stress at yield | 25 | MPa |
| stress at break | 37 | MPa |
| strain at break | 1000 | % |
| tensile modulus | 1000 | MPa |
| Flexural test | ||
| Flexural modulus | 1150 | MPa |
| Flexural strength | 26 | MPa |
| Izod impact notched | ||
| at 23 °C | 18 | kJ/m² |
| at -30 °C | 15 | kJ/m² |
| Hardness Shore D | 61 | – |
| ESCR (Strain Hardening), Gp | 23 | MPa |
| ESCR (10% Igepal CO-630), F50 | 200 | h |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190 °C and 5 kg | 0.35 | dg/min |
| at 190 °C and 21.6 kg | 9 | dg/min |
| Density | 952 | kg/m³ |
| THERMAL PROPERTIES | ||
| Heat deflection temperature | ||
| at 0.45 MPa (HDT/B) | 79 | °C |
| Vicat Softening Temperature | ||
| at 10 N (VST/A) | 127 | °C |
| DSC test | ||
| melting point | 132 | °C |
| enthalpy change | 200 | J/g |
B5403 is specially developed for blow molding, Jerry cans and drums.
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| 190°C & 21.6 kg load | 2.6 | g/10 min |
| Density at 23°C | 954 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| Tensile modulus | 1200 | MPa |
| Tensile Strength at Yield | 27 | MPa |
| Tensile Strain at Yield | 8 | % |
| Tensile Impact Strength at -30°C (Notched) | 290 | kJ/m² |
| Charpy Notched Impact Strength (-30°C, Type 1, Notch A) | 80 | kJ/m² |
| FNCT (3.5 MPa, 2 % Igepal BC/9, 80°C) | 14 | Hrs |
SABIC HDPE B5421 is typically used for packaging detergents, cleaners, shampoos and cosmetics at a high ESCR demand.
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190 °C and 2.16 kg | 0.16 | dg/min |
| at 190 °C and 5 kg | 0.89 | dg/min |
| at 190 °C and 21.6 kg | 20 | dg/min |
| Density | 954 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| Tensile test | ||
| stress at yield | 26 | MPa |
| stress at break | 27 | MPa |
| strain at break | 1000 | % |
| tensile modulus | 1050 | MPa |
| Flexural test | ||
| Flexural modulus | 1250 | MPa |
| Flexural strength | 27 | MPa |
| Izod impact notched | ||
| at 23 °C | 14 | kJ/m² |
| at -30 °C | 6 | kJ/m² |
| Hardness Shore D | 61 | – |
| ESCR (10% Igepal CO-630), F50 | 50 | h |
| THERMAL PROPERTIES | ||
| Heat deflection temperature | ||
| at 0.45 MPa (HDT/B) | 81 | °C |
| Vicat Softening Temperature | ||
| at 10 N (VST/A) | 127 | °C |
| DSC test | ||
| melting point | 135 | °C |
| enthalpy change | 205 | J/g |
A kind of medium molecular weight High Density Polyethylene copolymer. HDPE B5429 series grades offer excellent combination of toughness, stress cracking resistance, load bearing strength with easy processability, which is suitable for blow molding articles of small sizes.
| PROPERTIES | TYPICAL VALUES | UNITS |
| MECHANICAL PROPERTIES | ||
| 1% Secant Modulus | 1050 | MPa |
| Tensile Strength at Yield | 28 | MPa |
| Tensile Strength at Break | 19 | MPa |
| Tensile Elongation at Break | >500 | % |
| Flexural Strength | 25 | MPa |
| Flexural Modulus | 1000 | MPa |
| Izod Impact Strength | 180 | J/m |
| Hardness (Shore D) | 65 | – |
| ESCR (100% Igepal), F50 | 100 | Hrs |
| ESCR (10% Igepal), F50 | 60 | Hrs |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190°C and 2.16 kg | 0.3 | g/10 min |
| at 190°C and 21.6 kg | 29 | g/10 min |
| Density at 23°C | 954 | kg/m³ |
| THERMAL PROPERTIES | ||
| Vicat Softening Point | 124 | °C |
| Brittleness Temperature | <-75 | °C |
HDPE B5822 is designed for small blow molded bottles. The resin has easy flow, higher stiffness, good ESCR and sufficient impact strength.
| PROPERTIES | TYPICAL VALUES | UNITS |
| MECHANICAL PROPERTIES | ||
| Tensile modulus | 1350 | MPa |
| Tensile Stress at Yield | 28 | MPa |
| Tensile Strain at Yield | 7.5 | % |
| Tensile Impact Strength at -30°C (Notched) | 75 | kJ/m² |
| Charpy Notched Impact Strength (-30°C, Type 1, Notch A) | 6.5 | kJ/m² |
| Hardness (Shore D) | 64 | – |
| FNCT (3.5 MPa, 2 % Igepal BC/9, 80°C) | 8 | Hrs |
| ESCR | 150 | h |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190°C and 2.16 kg | 0.3 | g/10 min |
| at 190°C and 5 kg | 1.2 | g/10 min |
| at 190°C and 21.6 kg | 22 | g/10 min |
| Density at 23°C | 958 | kg/m³ |
SABIC HDPE B5823 is typically used for packaging the majority of household and industrial chemicals, such as detergents, cleaners, shampoos and cosmetics, as well as food packaging.
| PROPERTIES | TYPICAL VALUES | UNITS |
| MECHANICAL PROPERTIES | ||
| Tensile test | ||
| stress at yield | 28 | MPa |
| stress at break | 22 | MPa |
| strain at break | 1000 | % |
| tensile modulus | 1150 | MPa |
| Flexural test | ||
| Flexural modulus | 1400 | MPa |
| Flexural strength | 29 | MPa |
| Izod impact notched | ||
| at 23 °C | 12 | kJ/m² |
| at -30 °C | 6 | kJ/m² |
| Hardness Shore D | 63 | – |
| ESCR (10% Igepal CO-630), F50 | 45 | h |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190 °C and 2.16 kg | 0.16 | dg/min |
| at 190 °C and 5 kg | 0.89 | dg/min |
| at 190 °C and 21.6 kg | 23 | dg/min |
| Density | 958 | kg/m³ |
| THERMAL PROPERTIES | ||
| Heat deflection temperature | ||
| at 0.45 MPa (HDT/B) | 85 | °C |
| Vicat Softening Temperature | ||
| at 10 N (VST/A) | 128 | °C |
| DSC test | ||
| melting point | 133 | °C |
| enthalpy change | 215 | °C |
HDPE BM1052J is TNPP free, with excellent process ability. It has very high impact strength, stiffness and superior environmental stress crack resistance.
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| @ 190°C & 21.6 kg | 10 | g/10 min |
| @ 190°C and 5 kg | 0.38 | g/10 min |
| Density | ||
| @ 23°C | 952 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| 1% Secant Modulus | 1200 | MPa |
| Tensile strength | ||
| @ Yield | 28 | MPa |
| @ Break | 14 | MPa |
| Tensile Elongation at Break | >500 | % |
| Flexural Strength | 27 | MPa |
| Flexural Modulus | 905 | MPa |
| Izod Impact Strength | 270 | J/m |
| Hardness (Shore D) | 58 | – |
| ESCR (100% Igepal), F50 | >500 | Hrs |
| THERMAL PROPERTIES | ||
| Vicat Softening Point | 127 | °C |
| Brittleness Temperature | <-75 | °C |
Sabic HDPE F00952 is specifically designed for blown film extrusion. With excellent extrudability, high film strength and rigidity, it can be used for the manufacture of high strength grocery sacks, shopping bags and high quality thin films for multi wall sack liners. It is also the replacement for thin paper products.
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190 °C and 2.16 kg | 0.05 | dg/min |
| at 190 °C and 21.6 kg | 9 | dg/min |
| Density | 952 | kg/m³ |
| FILM PROPERTIES | ||
| Dart Impact F50 | 180 | g |
| Tear strength TD Elmendorf | 60 | g/µm |
| Tear strength MD Elmendorf | 12 | g/µm |
| Tensile test film | ||
| Strain at break TD | 550 | % |
| Strain at break MD | 400 | % |
| Stress at break MD | 60 | MPa |
| Stress at break TD | 56 | MPa |
| Modulus of elasticity TD | 1500 | MPa |
| Yield stress TD | 31 | MPa |
| Yield stress MD | 33 | MPa |
| Modulus of elasticity MD | 1250 | MPa |
| THERMAL PROPERTIES | ||
| Vicat Softening Temperature | ||
| Vicat softening temperature | 125 | °C |
FJ00952 HDPE is TNPP additive free grade. It has a unique combination of easy extrusion and high melt strength with strong physical properties which makes it suitable for producing thin films with excellent strength and rigidity.
| PROPERTIES | TYPICAL VALUES | UNITS |
| FILM PROPERTIES | ||
| Tensile Properties | ||
| stress at break, MD | 60 | MPa |
| stress at break, TD | 56 | MPa |
| strain at break, MD | 400 | % |
| strain at break, TD | 550 | % |
| stress at yield, MD | 33 | MPa |
| stress at yield, TD | 31 | MPa |
| 1% secant modulus, MD | 1250 | MPa |
| 1% secant modulus, TD | 1500 | MPa |
| Elmendorf Tear Strength | ||
| MD | 12 | g |
| TD | 60 | g |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190°C and 2.16 kg | 0.05 | g/10 min |
| at 190°C and 21.6 kg | 9 | g/10 min |
| Density | ||
| at 23°C | 952 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| Dart Impact Strength | 180 | g/µm |
| THERMAL PROPERTIES | ||
| Vicat Softening Temperature | 125 | °C |
SABIC HDPE Fi0750 is typically used for blown film applications.
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190 °C and 21.6 kg | 7.5 | g/10 min |
| at 190 °C and 5 kg | 0.22 | g/10 min |
| Density | 950 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| Hardness Shore D | 62 | – |
| FILM PROPERTIES | ||
| Tensile Properties | ||
| stress at break, MD | 50 | MPa |
| stress at break, TD | 45 | MPa |
| strain at break, MD | 400 | % |
| strain at break, TD | 450 | % |
| Dart Impact Strength | ||
| F50 | 240 | g |
| Elmendorf Tear Strength | ||
| MD | 250 | mN |
| TD | 450 | mN |
| THERMAL PROPERTIES | ||
| Brittleness Temperature | <-80 | °C |
| Vicat Softening Temperature | ||
| at 50 N (VST/B) | 75 | °C |
SABIC HDPE F04660 is a homopolymer film grade with a broad processing window and high stiffness.
| PROPERTIES | TYPICAL VALUES | UNITS |
| FILM PROPERTIES | ||
| Tensile Properties | ||
| stress at break, MD | 67 | MPa |
| stress at break, TD | 37 | MPa |
| strain at break, MD | 490 | % |
| strain at break, TD | 3 | % |
| 1% secant modulus, MD | 1250 | MPa |
| 1% secant modulus, TD | 1700 | MPa |
| Elmendorf Tear Strength | ||
| MD | 10 | g |
| TD | 800 | g |
| Dart Impact Strength | ||
| F50 | <20 | g |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190°C and 2.16 kg | 0.7 | g/10 min |
| at 190°C and 21.6 kg | 46 | g/10 min |
| Density | ||
| at 23°C | 961 | kg/m³ |
| THERMAL PROPERTIES | ||
| Vicat Softening Temperature | 129 | °C |
SABIC HDPE M1053 is an easy-to-process, tough grade with good resistance to environmental stress cracking and low notch sensitivity. SABIC HDPE M1053 is typically used for caps, closures and pails.
| PROPERTIES | TYPICAL VALUES | UNITS |
| MECHANICAL PROPERTIES | ||
| Tensile test | ||
| stress at yield | 26 | MPa |
| stress at break | 16 | MPa |
| strain at break | 200 | % |
| tensile modulus | 1100 | MPa |
| Flexural test | ||
| Flexural modulus | 1200 | MPa |
| Flexural strength | 26 | MPa |
| Izod impact notched | ||
| at 23 °C | 3 | kJ/m² |
| Hardness Shore D | 61 | – |
| ESCR on Caps | 25 | h |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190 °C and 2.16 kg | 10 | dg/min |
| at 190 °C and 5 kg | 28 | dg/min |
| Density | 953 | kg/m³ |
| THERMAL PROPERTIES | ||
| Heat deflection temperature | ||
| at 0.45 MPa (HDT/B) | 81 | °C |
| Vicat Softening Temperature | ||
| at 10 N (VST/A) | 124 | °C |
| DSC test | ||
| melting point | 132 | °C |
| enthalpy change | 203 | J/g |
With narrow molecular weight distribution, HDPE M200056 is suitable for injection molding applications. It is designed to offer good flow properties, low warp age with good dimensional stability and high gloss.
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190°C and 2.16 kg | 20 | g/10 min |
| Density at 23°C | 956 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| 1% Secant Modulus | 800 | MPa |
| Tensile Strength at Yield | 24 | MPa |
| Tensile Strength at Break | 12 | MPa |
| Tensile Elongation at Break | >200 | % |
| Flexural Strength | 23 | MPa |
| Flexural Modulus | 825 | MPa |
| Izod Impact Strength | 30 | J/m |
| Hardness (Shore D) | 60 | – |
| ESCR (100% Igepal), F50 | 3 | Hrs |
| ESCR (10% Igepal), F50 | 2 | Hrs |
| THERMAL PROPERTIES | ||
| Vicat Softening Point | 124 | °C |
| Brittleness Temperature | <-75 | °C |
M40053S is a UV stabilized HDPE grade suitable for injection molding applications.
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190°C and 2.16 kg | 4 | g/10 min |
| Density at 23°C | 953 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| 1% Secant Modulus | 900 | MPa |
| Tensile Strength at Yield | 23 | MPa |
| Tensile Strength at Break | 21 | MPa |
| Tensile Elongation at Break | >800 | % |
| Flexural Strength | 21 | MPa |
| Flexural Modulus | 800 | MPa |
| Izod Impact Strength | 150 | J/m |
| Hardness (Shore D) | 60 | – |
| ESCR (100% Igepal), F50 | 7 | Hrs |
| ESCR (10% Igepal), F50 | 4 | Hrs |
| THERMAL PROPERTIES | ||
| Vicat Softening Point | 125 | °C |
| Brittleness Temperature | <-75 | °C |
With good rigidity, toughness and low warpage, M80064 HDPE is suitable for injection molding applications.
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190°C and 2.16 kg | 8 | g/10 min |
| Density at 23°C | 964 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| 1% Secant Modulus | 950 | MPa |
| Tensile Strength at Yield | 26 | MPa |
| Tensile Strength at Break | 18 | MPa |
| Tensile Elongation at Break | >800 | % |
| Flexural Strength | 42 | MPa |
| Flexural Modulus | 1650 | MPa |
| Izod Impact Strength | 75 | J/m |
| Hardness (Shore D) | 62 | – |
| ESCR (100% Igepal), F50 | 3 | Hrs |
| ESCR (10% Igepal), F50 | 2 | Hrs |
| THERMAL PROPERTIES | ||
| Vicat Softening Point | 125 | °C |
| Brittleness Temperature | <-75 | °C |
HDPE M80064S is a UV stabilized. It is typically used for injection molding applications that require rigidity, toughness and warp resistance.
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190°C and 2.16 kg | 8 | g/10 min |
| Density at 23°C | 964 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| 1% Secant Modulus | 950 | MPa |
| Tensile Strength at Yield | 26 | MPa |
| Tensile Strength at Break | 18 | MPa |
| Tensile Elongation at Break | >800 | % |
| Flexural Strength | 42 | MPa |
| Flexural Modulus | 1650 | MPa |
| Izod Impact Strength | 75 | J/m |
| Hardness (Shore D) | 62 | – |
| ESCR (100% Igepal), F50 | 3 | Hrs |
| ESCR (10% Igepal), F50 | 2 | Hrs |
| THERMAL PROPERTIES | ||
| Vicat Softening Point | 125 | °C |
| Brittleness Temperature | <-75 | °C |
Sabic HDPE 6006 is a kind of black compound multimodal high density polyethylene, pecifically designed for pressure Pipe applications. It provides excellent stress crack resistance properties combined with very good long term hydrostatic strength.
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| @ 190°C & 5 kg load | 0.23 | g/10 min |
| @ 190°C & 21.6 kg load | 6.2 | g/10 min |
| Carbon black content | 2.25 | % |
| Density at 23°C | 959 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| Tensile Strength at Yield | 23 | MPa |
| Tensile Elongation at Yield | 9 | % |
| Tensile modulus | 900 | MPa |
| Charpy Impact Notched @ 23°C | 26 | kJ/m² |
| Charpy Impact Notched @ -30°C | 13 | kJ/m² |
| Hardness (Shore D) | 63 | – |
| THERMAL PROPERTIES | ||
| Vicat Softening Point @ 50N (VST/B) | 74 | °C |
| OIT (210°C) | >20 | Minutes |
P6006AD HDPE is black compound multimodal high density polyethylene, specially designed for pressure pipe applications.
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| @ 190°C & 5 kg load | 0.23 | g/10 min |
| @ 190°C & 21.6 kg load | 6.4 | g/10 min |
| Carbon black content | 2.25 | % |
| Density at 23°C | 959 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| Tensile Strength at Yield | 23 | MPa |
| Tensile Elongation @ Break | >350 | % |
| Tensile modulus | 900 | MPa |
| Tensile creep Moduls @ 100h | 360 | MPa |
| Charpy Notched Impact Strength @ 23°C | 26 | kJ/m² |
| THERMAL PROPERTIES | ||
| OIT (210°C) | >30 | Minutes |
Sabic HDPE 952 is pecifically designed for non-pressure pipe extrusion application.
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| @ 190°C & 5 kg load | 0.33 | g/10 min |
| @ 190°C & 21.6 kg load | 9 | g/10 min |
| Density at 23°C | 952 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| Tensile Strength at Yield | 24 | MPa |
| Tensile Elongation at Yield | 9 | % |
| Tensile modulus | 1500 | MPa |
| Charpy Impact Notched @ 23°C | 250 | J/m |
| Hardness (Shore D) | 55 | – |
| THERMAL PROPERTIES | ||
| Vicat Softening Point | 73 | °C |
Except for the models listed above, we can also supply other models of Sabic HDPE. Feel free to inquiry us the models you need, we will reply you quickly.
As a leading reliable supplier of plastic chemicals, Chemate can guarantee the best price and good quality. Meawhile, we can also supply other brands of HDPE, check more from our website or contact us for quotation.