Sabic LDPE

Hot Sale Models of Sabic LDPE

Sabic HP2022JN

HP2022JN LDPE is suitable for general-purpose packaging. They exhibit better draw down, good optical and mechanical properties. It contains slip and antiblock additives. It can be used for thin shrink film, lamination film, producing bags, textile packaging, soft goods packaging, general-purpose bags with good optics and t-shirts carrier bags.

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
POLYMER PROPERTIES
Melt Flow Rate (MFR)
at 190°C and 2.16 kg	2.0	g/10 min	ASTM D1238
Density
at 23°C	922	kg/m³	ASTM D1505
MECHANICAL PROPERTIES
Dart Impact Strength	2	g/µm	ASTM D1709
OPTICAL PROPERTIES
Haze (1)	10	%	ASTM D1003
Gloss
at 45°	55	–	ASTM D2457
FILM PROPERTIES
Tensile Properties
stress at break, MD	29	MPa	ASTM D882
stress at break, TD	15	MPa	ASTM D882
strain at break, MD	120	%	ASTM D882
strain at break, TD	530	%	ASTM D882
stress at yield, MD	11	MPa	ASTM D882
stress at yield, TD	11	MPa	ASTM D882
1% secant modulus, MD	180	MPa	ASTM D882
1% secant modulus, TD	230	MPa	ASTM D882
Tear Resistance
MD	18	g/µm	ASTM D1922
TD	4	g/µm	ASTM D1922
THERMAL PROPERTIES
Vicat Softening Temperature	92	°C	ASTM D1525

Sabic 2022NDF

2022NDF LDPE is a grade typically used in foam applications. It is without slip and anti-block additives. This grades is ideally suitable for foaming processes using both physical and chemical blowing agents.

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
POLYMER PROPERTIES
Melt Flow Rate (MFR)
at 190°C and 2.16 kg	2.0	g/10 min	ASTM D1238
Density
at 23°C	922	kg/m³	ASTM D1505
THERMAL PROPERTIES
Vicat Softening Temperature	92	°C	ASTM D1525
Crystallization Temperature	95	°C	ISO 11357-3
Avg. Heat of Fusion	113	J/g	ISO 11357-3
Melting Point	110	°C	SABIC method

Sabic HP2023JN

HP2023JN LDPE is suitable for general-purpose packaging. It exhibits better draw down, good optical and mechanical properties. It contains slip and antiblock additives.

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
POLYMER PROPERTIES
Melt Flow Rate (MFR)
at 190°C and 2.16 kg	2.0	g/10 min	ASTM D1238
Density
at 23°C	923	kg/m³	ASTM D1505
OPTICAL PROPERTIES
Haze	8	%	ASTM D1003
Gloss
at 45°	61	%	ASTM D2457
FILM PROPERTIES
Tensile Properties
stress at break, MD	20	MPa	ASTM D882
stress at break, TD	15	MPa	ASTM D882
strain at break, MD	300	%	ASTM D882
strain at break, TD	588	%	ASTM D882
stress at yield, MD	12	MPa	ASTM D882
stress at yield, TD	12	MPa	ASTM D882
1% secant modulus, MD	235	MPa	ASTM D882
1% secant modulus, TD	271	MPa	ASTM D882
Tear Resistance
MD	15	g/µm	ASTM D1922
TD	11	g/µm	ASTM D1922
Dart Impact F50	2	g	ASTM D1709
THERMAL PROPERTIES
Vicat Softening Temperature	92	°C	ASTM D1525

SABIC HP2023NN

HP2023NN LDPE is suitable for general-purpose packaging. It exhibits better draw down, good optical and mechanical properties. It contains no slip, no antiblock and no antioxidant additives.

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
POLYMER PROPERTIES
Melt Flow Rate (MFR)
190°C and 2.16 kg	2.0	g/10 min	ASTM D1238
Density
at 23°C	923	kg/m³	ASTM D1505
OPTICAL PROPERTIES
Haze	8	%	ASTM D1003
Gloss
at 45°	61	%	ASTM D2457
FILM PROPERTIES
Tensile Properties
stress at break, MD	20	MPa	ASTM D882
stress at break, TD	15	MPa	ASTM D882
strain at break, MD	300	%	ASTM D882
strain at break, TD	588	%	ASTM D882
stress at yield, MD	12	MPa	ASTM D882
stress at yield, TD	12	MPa	ASTM D882
1% secant modulus, MD	235	MPa	ASTM D882
1% secant modulus, TD	271	MPa	ASTM D882
Tear Resistance
MD	15	g/µm	ASTM D1922
TD	11	g/µm	ASTM D1922
Dart Impact F50	2	g	ASTM D1709
THERMAL PROPERTIES
Vicat Softening Temperature	92	°C	ASTM D1525

Sabic 4024N

HP4024N LDPE is suitable for producing general-purpose films and it gives excellent processability and optical properties with good mechanical properties. No slip and no antiblock additives. It can be used for high clarity laundry bags, textile wrapping films, produce bags, zip lock bags and master batch.

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
POLYMER PROPERTIES
Melt Flow Rate (MFR)
at 190°C and 2.16 kg	4.0	g/10 min	ASTM D1238
Density
at 23°C	923	kg/m³	ASTM D1505
MECHANICAL PROPERTIES
Dart Impact Strength	2	g/µm	ASTM D1709
OPTICAL PROPERTIES
Haze	6	%	ASTM D1003
Gloss
at 45°	68	–	ASTM D2457
FILM PROPERTIES
Tensile Properties
stress at break, MD	32	MPa	ASTM D882
stress at break, TD	24	MPa	ASTM D882
strain at break, MD	265	%	ASTM D882
strain at break, TD	600	%	ASTM D882
stress at yield, MD	10	MPa	ASTM D882
stress at yield, TD	10	MPa	ASTM D882
1% secant modulus, MD	277	MPa	ASTM D882
1% secant modulus, TD	224	MPa	ASTM D882
Tear Resistance
MD	10	g/µm	ASTM D1922
TD	14	g/µm	ASTM D1922
THERMAL PROPERTIES
Vicat Softening Point	92	°C	ASTM D1525

SABIC HP4024WN

HP4024WN LDPE is suitable for producing general-purpose films and it gives excellent processability and optical properties with good mechanical properties. Contain slip and antiblock additives.

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
POLYMER PROPERTIES
Melt Flow Rate (MFR)
at 190°C and 2.16 kg	4.0	g/10 min	ASTM D1238
Density
at 23°C	923	kg/m³	ASTM D1505
MECHANICAL PROPERTIES
Dart Impact Strength	2	g/µm	ASTM D1709
OPTICAL PROPERTIES
Haze	6	%	ASTM D1003
Gloss
at 45°	68	%	ASTM D2457
FILM PROPERTIES
Tensile Properties
stress at break, MD	32	MPa	ASTM D882
stress at break, TD	24	MPa	ASTM D882
strain at break, MD	265	%	ASTM D882
strain at break, TD	600	%	ASTM D882
stress at yield, MD	10	MPa	ASTM D882
stress at yield, TD	10	MPa	ASTM D882
1% secant modulus, MD	277	MPa	ASTM D882
1% secant modulus, TD	224	MPa	ASTM D882
Tear Resistance
MD	10	g/µm	ASTM D1922
TD	14	g/µm	ASTM D1922
THERMAL PROPERTIES
Vicat Softening Temperature	92	°C	ASTM D1525

SABIC HP4024ZN

HP4024ZN LDPE is suitable for producing general-purpose films and it gives excellent processability and optical properties with good mechanical properties. Contain high level of slip and antiblock additives.

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
POLYMER PROPERTIES
Melt Flow Rate (MFR)
at 190°C and 2.16 kg	4.0	g/10 min	ASTM D1238
Density
at 23°C	923	kg/m³	ASTM D1505
MECHANICAL PROPERTIES
Dart Impact Strength	2	g/µm	ASTM D1709
OPTICAL PROPERTIES
Haze (1)	6	%	ASTM D1003
Gloss
at 45°	68	–	ASTM D2457
FILM PROPERTIES
Tensile Properties
stress at break, MD	32	MPa	ASTM D882
stress at break, TD	24	MPa	ASTM D882
strain at break, MD	265	%	ASTM D882
strain at break, TD	600	%	ASTM D882
stress at yield, MD	10	MPa	ASTM D882
stress at yield, TD	10	MPa	ASTM D882
1% secant modulus, MD	277	MPa	ASTM D882
1% secant modulus, TD	224	MPa	ASTM D882
Tear Resistance
MD	10	g/µm	ASTM D1922
TD	14	g/µm	ASTM D1922
THERMAL PROPERTIES
Vicat Softening Temperature	92	°C	ASTM D1525

Buy Sabic LDPE from Chemate