BJ368MO is a heterophasic copolymer characterized by very high flow, and optimum combination of high stiffness and impact strength. The material is nucleated with Borstar Nucleation Technology (BNT). Flow properties, nucleation and good stiffness give potential for cycle time reduction. The material has both good antistatic performance and mould release properties.
| Property | Typical value | Unit | Test method |
| Density | 905 | kg/m³ | ISO 1183-1 |
| Melt flow rate (230 °C/2.16 kg) | 70 | g/10min | ISO 1133-1 |
| Flexural modulus | 1500 | MPa | ISO 178 |
| Tensile modulus (1 mm/min) | 1500 | MPa | ISO 527-2 |
| Tensile strain at yield (50 mm/min) | 4 | % | ISO 527-2 |
| Tensile stress at yield (50 mm/min) | 25 | MPa | ISO 527-2 |
| Charpy impact strength, notched (23 °C) | 5.5 | kJ/m² | ISO 179-1/1eA |
| Charpy impact strength, notched (-20 °C) | 3.5 | kJ/m² | ISO 179-1/1eA |
| Heat deflection temperature A (1.80 MPa) | 102 | °C | ISO 75-2 |