HDPE 25455N High Density Resin is a narrow molecular weight distribution copolymer designed to offer good ESCR and gloss with excellent toughness.
Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Density | 0.955 | g/cm³ | 0.955 | g/cm³ | ASTM D792 |
Base Density 1 | 0.955 | g/cm³ | 0.955 | g/cm³ | Dow Method |
Melt Index (190°C/2.16 kg) | 25 | g/10 min | 25 | g/10 min | ASTM D1238 |
Environmental Stress-Cracking Resistance (ESCR) | ASTM D1693 | ||||
122°F (50°C), 100% Igepal, F50 | 1.00 | hr | 1.00 | hr | |
Mechanical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Tensile Strength | ASTM D638 | ||||
Yield | 3700 | psi | 25.5 | MPa | |
Break | 2000 | psi | 13.8 | MPa | |
Tensile Elongation | ASTM D638 | ||||
Yield | 6.0 | % | 6.0 | % | |
Break | 200 | % | 200 | % | |
Flexural Modulus - 2% Secant | 136000 | psi | 938 | MPa | ASTM D790B |
Impact | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Tensile Impact Strength 2 | 60.0 | ft·lb/in² | 126 | kJ/m² | ASTM D1822 |
Hardness | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Durometer Hardness (Shore D) | 59 | 59 | ASTM D2240 | ||
Thermal | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Deflection Temperature Under Load | ASTM D648 | ||||
66 psi (0.45 MPa), Unannealed | 153 | °F | 67.2 | °C | |
Brittleness Temperature | < -105 | °F | < -76.1 | °C | ASTM D746 |
Vicat Softening Temperature | 262 | °F | 128 | °C | ASTM D1525 |
Melting Temperature (DSC) | 264 | °F | 129 | °C | Dow Method |
Peak Crystallization Temperature (DSC) | 241 | °F | 116 | °C | Dow Method |
- For toys and housewares.
- Good low temperature impact strength, gloss and excellent toughness.
Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Density | 0.950 | g/cm³ | 0.950 | g/cm³ | ASTM D792 |
Base Density 1 | 0.950 | g/cm³ | 0.950 | g/cm³ | Dow Method |
Melt Index (190°C/2.16 kg) | 17 | g/10 min | 17 | g/10 min | ASTM D1238 |
Environmental Stress-Cracking Resistance (ESCR) | ASTM D1693 | ||||
122°F (50°C), 100% Igepal, F50 | 3.00 | hr | 3.00 | hr | |
Mechanical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Tensile Strength | ASTM D638 | ||||
Yield | 3300 | psi | 22.8 | MPa | |
Break | 1800 | psi | 12.4 | MPa | |
Tensile Elongation | ASTM D638 | ||||
Yield | 3.0 | % | 3.0 | % | |
Break | 300 | % | 300 | % | |
Flexural Modulus - 2% Secant | 114000 | psi | 786 | MPa | ASTM D790B |
Impact | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Tensile Impact Strength 2 | 140 | ft·lb/in² | 294 | kJ/m² | ASTM D1822 |
Hardness | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Durometer Hardness | 62 | 62 | ASTM D2240 | ||
Thermal | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Deflection Temperature Under Load | ASTM D648 | ||||
66 psi (0.45 MPa), Unannealed | 149 | °F | 65.0 | °C | |
Brittleness Temperature | < -105 | °F | < -76.1 | °C | ASTM D746 |
Vicat Softening Temperature | 259 | °F | 126 | °C | ASTM D1525 |
Melting Temperature (DSC) | 262 | °F | 128 | °C | Dow Method |
Peak Crystallization Temperature (DSC) | 239 | °F | 115 | °C | Dow Method |
HDPE 25055E Resin is a very narrow molecular weight distribution resin, developed to impart excellent mechanical properties, high gloss and high surface finishing to injection moulded parts, while providing easy processing.
Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Density | 0.955 | g/cm³ | 0.955 | g/cm³ | ASTM D792 |
Melt Index | ISO 1133 | ||||
190°C/2.16 kg | 25 | g/10 min | 25 | g/10 min | |
190°C/5.0 kg | 62 | g/10 min | 62 | g/10 min | |
Spiral Flow 1, 2 | 42.9 | in | 109 | cm | Dow Method |
Molding Shrinkage - Flow | 0.021 | in/in | 2.1 | % | ASTM D955 |
Environmental Stress-C racking Resistance (ESCR) | ASTM D1693 | ||||
100% Antarox CO-630, Compression Molded | 0.700 | hr | 0.700 | hr |
Mechanical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Tensile Strength Yield, Compression Molded | 3630 | psi | 25.0 | MPa | ASTM D638 |
Break, Compression Molded | 3920 | psi | 27.0 | MPa | |
Tensile Elongation Break, Compression Molded | 200 | % | 200 | % | ASTM D638 |
Flexural Modulus - 2% Secant 126000 | psi | 870 | MPa | ASTM D790 | |
Impact | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Tensile Impact Strength (Compression Molded) | 26.2 | ft·lb/in² | 55.0 | kJ/m² | ASTM D1822 |
Hardness | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Shore 65 | 65 | ISO 868 | |||
Thermal | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Vicat Softening Temperature | 255 | °F | 124 | °C | ISO 306/A |
Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Density | 0.964 | g/cm³ | 0.964 | g/cm³ | ASTM D792 |
Melt Index | ISO 1133 | ||||
190°C/2.16 kg | 8.0 | g/10 min | 8.0 | g/10 min | |
190°C/5.0 kg | 22 | g/10 min | 22 | g/10 min | |
Spiral Flow 1, 2 | 28.9 | in | 73.5 | cm | Dow Method |
Molding Shrinkage - Flow | 0.021 | in/in | 2.1 | % | ASTM D955 |
Environmental Stress-Cracking Resistance (ESCR) | ASTM D1693 | ||||
100% Antarox CO-630, Compression Molded | 2.50 | hr | 2.50 | hr |
Buy DOW HDPE from Chemate
As a leading reliable supplier of plastic chemicals, Chemate can guarantee the best price and good quality. Meawhile, we can also supply other brands of high density polyethylene resin, check more from our website or contact us for help.