ExxonMobil EVA 25028 resins are a high vinyl acetate copolymers for specialty compounding applications and hot melt adhesives.
Additive
| Grade | Antiblock | Slip | Thermal Stabilizer |
| EVA 25028.12 | NO | NO | YES |
| EVA 25028.CM | NO | NO | NO |
Applications
Compounding, hot melt adhesives, masterbatch base resin.
| Resin Properties | Typical Value (English) | Typical Value (SJ) | Test Based On |
|---|---|---|---|
| Density | 0.952 g/cm³ | 0.952 g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (125°C/2.16 kg) | 25 g/10 min | 25 g/10 min | ExxonMobil Method |
| Vinyl Acetate Content | 27.6 wt% | 27.6 wt% | ExxonMobil Method |
| Peak Melting Temperature | 158 °F | 70 °C | ExxonMobil Method |
| Thermal | |||
| Vicat Softening Temperature | 104 °F | 40.0 °C | ExxonMobil Method |
| Molded Properties | |||
| Tensile Strength at Break | 740 psi | 5.1 MPa | ExxonMobil Method |
| Elongation at Break | 664 % | 664 % | ExxonMobil Method |
| Flexural Modulus – 1% Secant | 2600 psi | 18 MPa | ExxonMobil Method |
| Durometer Hardness | ExxonMobil Method | ||
| Shore A, 15 sec | 78 | 78 | ExxonMobil Method |
| Shore D, 15 sec | 21 | 21 | |