Exceed™ m 1018.RA mLLDPE
Exceed™ m 1018.RA mLLDPE is an ethylene 1-hexene copolymer resin. Films that incorporate Exceed™ m 1018.RA can enable outstanding tensile, impact strength and puncture performance. These superior strength properties, along with excellent drawability, can support downgauging in film applications. Fluoropolymers, or fluorine-containing compounds, and TNPP are not intentionally added to Exceed™ m 1018.RA.
Technical Specifications of Exceed™ m 1018.RA mLLDPE
| Properties | Typical value | Test method |
| Density | 0.918g/cm³ | ASTM D792 |
| Melt index | 1.0g/10min (190℃/2.16kg) | ASTM D1238 |
| Peak melting temperature | 118℃ | ExxonMobil method |
| Tensile strength at yield MD | 8.7 Mpa | ASTM D882 |
| Tensile strength at yield TD | 8.8 Mpa | ASTM D882 |
| Tensile strength at break MD | 60 Mpa | ASTM D882 |
| Tensile strength at break TD | 60 Mpa | ASTM D882 |
| Elongation at break MD | 500% | ASTM D882 |
| Elongation at break TD | 640% | ASTM D882 |
| Secant modulus MD – 1% secant | 170 Mpa | ASTM D882 |
| Secant modulus TD – 1% secant | 180 Mpa | ASTM D882 |
| Dart drop impact | 550g | ASTM D1709A |
| Elmendorf tear strength MD | 220g | ASTM D1922 |
| Elmendorf tear strength TD | 370g | ASTM D1922 |
| Puncture force | 59N | ExxonMobil method |
| Puncture energy | 5.5J | ExxonMobil method |
| Gloss (45℃) | 43 | ASTM D2457 |
| Haze | 16% | ASTM D1003 |
What Are Main Applications of Exceed™ m 1018.RA?
Agricultural film, bag in box, barrier food packaging, blown film, blown stretch film, bread bags, food packaging.
Form fill and seal packaging, freezer film, general packaging, heavy duty bags, industrial packaging, lamination film, multilayer packaging film.
Overwrap film, packaging films, premium trash bags, stand up pouches, trash bags, trash can liners.
What are the superior properties of Exceed™ m 1018.RA?
>> Exceptional mechanical toughness and outstanding impact and puncture resistance
Tested dart impact strength >550g, puncture strength up to approximately 57.8N, and excellent tensile and tear strength. It maintains stable breakage and tensile strength even in thin-film processing scenarios. Even in ultra-thin film products, it balances flexibility and structural stability, providing core support for material reduction and cost savings.
>> Excellent processing performance and compatibility with high-speed production lines
Based on its well-defined molecular structure, Exceed™ m 1018.RA has moderate melt strength, excellent blown film forming stability, strong bubble stability, and high thickness uniformity, effectively reducing scrap rates during production. It is compatible with high-speed blown film, bag making, and filling integrated production lines, perfectly matching high-speed molding, filling, and sealing packaging processes.
>> Weather and low-temperature resistance, suitable for harsh applications
The product possesses excellent low-temperature toughness and environmental tolerance. It does not become brittle, harden, or crack under low-temperature conditions, making it stable and suitable for low-temperature applications such as frozen food packaging and cold chain storage films. The material is also tensile and abrasion resistant, exhibiting excellent anti-aging and anti-deformation capabilities in daily use.
>> Superior appearance and safety performance
The film prepared by 1018.RA mLLDPE boasts high transparency, low haze, a smooth and even surface free of obvious crystal points and streaks, resulting in a superior visual texture that meets the aesthetic requirements of high-end packaging. Furthermore, the product complies with general food contact and environmental protection standards, with no harmful additives leaching. Its fluorine-free, environmentally friendly formula is safe and harmless, making it suitable for direct application in intimate packaging scenarios such as food and daily necessities.