| Property |
ISO Method |
Test Condition |
Unit |
PA-777D Value |
| Melt Flow Index |
1133 |
220℃×10KG |
ml/10 min |
5.5 |
| Mass Density |
1183 |
23℃ |
g/cm³ |
1.06 |
| Mechanical Properties |
|
|
|
|
| • Tensile Strength (Yield) |
527 |
50 mm/min |
MPa |
45 |
| • Tensile Strength (Break) |
527 |
50 mm/min |
MPa |
33 |
| • Tensile Elongation |
527 |
50 mm/min |
% |
34 |
| • Flexural Strength |
178 |
2 mm/min |
MPa |
73 |
| • Flexural Modulus |
– |
2 mm/min |
GPa |
2.3 |
| Impact Resistance |
|
|
|
|
| • Izod (23℃ Notched) |
180/1A |
23℃ |
KJ/m² |
13 |
| • Izod (-30℃ Notched) |
180/1A |
-30℃ |
KJ/m² |
7 |
| • Charpy (23℃ Notched) |
179 |
23℃ |
KJ/m² |
14 |
| • Charpy (-30℃ Notched) |
179 |
-30℃ |
KJ/m² |
7 |
| Thermal Properties |
|
|
|
|
| • Vicat Softening Temp (1Kg) |
306 |
50℃/hr |
℃ |
124 |
| • Vicat Softening Temp (5Kg) |
306 |
50℃/hr |
℃ |
117 |
| • HDT (1.8 MPa Unannealed) |
75/A |
1.8 MPa |
℃ |
97 |
| • HDT (1.8 MPa Annealed) |
75/A |
1.8 MPa |
℃ |
117 |
| • CTE |
11359 |
– |
1/℃ |
8.3×10⁻⁵ |
| Safety & Processing |
|
|
|
|
| • Flammability (UL-94) |
– |
– |
Rating |
1.5mm HB |
| • Mold Shrinkage |
294-4 |
– |
% |
0.3-0.6 |
| • Material Symbol |
1043 |
– |
Designation |
>ABS< |