Lotrène FB3003 is an additive free grade, produced by an autoclave high pressure process, mainly recommended for heavy duty film applications.
Lotrene® FB3003 LDPE TDS
POLYMER PROPERTIES | Value | UNIT | TEST METHOD |
Melt Flow Index | 0.30 | g/10 min. | ASTM D1238- |
Density @ 23 °C | 0.920 | g/cm3 | ASTM D1505- |
Crystalline Melting Point | 109 | °C | ASTM E794- |
Vicat Softening Point | 96 | °C | ASTM D1525- |
FILM PROPERTIES | Value | UNIT | TEST METHOD |
Tensile Strength @ Yield MD/ TD | 14/11 | MPa | ASTM D882- |
Tensile Strength @ Break MD/ TD | 30/27 | MPa | ASTM D882- |
Elongation @ Break MD/ TD | 250/555 | % | ASTM D882- |
Tear resistance MD/ TD | 21/26 | N/mm | ASTM D1922- |
Impact Strength, F 50 | 175 | g | ASTM D1709- |
Puncture Force | 60 | N | Internal Method |
| 0.50 | | ASTM D1894- |
Haze | 34 | % | ASTM D1003- |
Gloss @ °45 | 19 | | ASTM D2457- |
Lotrène FB5026 is a grade produced by autoclave high pressure process and is mainly recommended for medium duty film applications with good optical properties. It contains slip agent (target: 300 ppm erucamide).
Lotrene® FB5026 LDPE TDS
POLYMER PROPERTIES | VALUE | UNIT | TEST METHOD |
Melt Flow Index | 0.60 | g/10 min. | ASTM D1238- |
Density @ 23 °C | 0.920 | g/cm3 | ASTM D1505- |
Crystalline Melting Point | 108 | °C | ASTM E794- |
Vicat Softening Point | 93 | °C | ASTM D1525- |
FILM PROPERTIES | VALUE | UNIT | TEST METHOD |
Tensile Strength @ Yield MD/ TD | 12/11 | MPa | ASTM D882- |
Tensile Strength @ Break MD/ TD | 34/28 | MPa | ASTM D882- |
Elongation @ Break MD/ TD | 325/615 | % | ASTM D882- |
Impact Strength, F 50 | 175 | g | ASTM D1709- |
Tear resistance MD/ TD | 34/25 | N/mm | ASTM D- 1922 |
Puncture Force | 43 | N | Internal Method |
| 0.08 | - | ASTM D1894- |
Haze | 16 | % | ASTM D1003- |
Gloss °(@ 45 °) | 41 | - | ASTM D2457- |
Lotrène FD0270 is an additive free grade mainly recommended for the extrusion of thin film for light and medium duty applications.
Lotrene® FD0270 LDPE TDS
POLYMER PROPERTIES | VALUE | UNIT | TEST METHOD |
Melt Flow Index | 2.4 | g/10 min. | ASTM D1238- |
Density @ 23 °C | 0.923 | g/cm3 | ASTM D792- |
Crystalline Melting Point | 112 | °C | ASTM E794- |
Vicat Softening Point | 96 | °C | ASTM D1525- |
FILM PROPERTIES | VALUE | UNIT | TEST METHOD |
Tensile Strength @ Yield MD/ TD | 12/12 | MPa | ASTM D882- |
Tensile Strength @ Break MD/ TD | 28/24 | MPa | ASTM D882- |
Elongation @ Break MD/ TD | 430/660 | % | ASTM D882- |
Tear resistance MD/ TD | 90/70 | N/mm | ASTM D- 1922 |
Puncture Force | 50 | N | Internal Method |
Impact Strength, F 50 | 85 | g | ASTM D1709- |
| 1.2 | | ASTM D1894- |
Haze | 5.5 | % | ASTM D1003- |
Gloss (@ 45 °) | 73 | | ASTM D2457- |
Lotrène FD0274 is mainly recommended for the extrusion of thin film for light and medium duty applications. It contains both slip additives (target 600 ppm erucamide) and anti blocking additives (target 900 ppm) as well as antioxidants.
Lotrene® FD0274 LDPE TDS
POLYMER PROPERTIES | VALUE | UNIT | TEST METHOD |
Melt Flow Index | 2.4 | g/10 min. | ASTM D1238- |
Density @ 23 °C | 0.923 | g/cm3 | ASTM D1505- |
Crystalline Melting Point | 108 | °C | ASTM E794- |
Vicat Softening Point | 89 | °C | ASTM D1525- |
FILM PROPERTIES | VALUE | UNIT | TEST METHOD |
Tensile Strength @ Yield MD/ TD | 11/11 | MPa | ASTM D882- |
Tensile Strength @ Break MD/ TD | 24/22 | MPa | ASTM D882- |
Elongation @ Break MD/ TD | 300/600 | % | ASTM D882- |
Impact Strength, F 50 | 110 | g | ASTM D1709- |
Tear resistance MD/ TD | 65/35 | N/mm | ASTM D- 1922 |
Puncture Force | 30 | N | Internal Method |
| 0.12 | | ASTM D1894- |
Haze | 8.0 | % | ASTM D1003- |
Gloss @ °45 | 59 | | ASTM D2457- |
Lotrène FD0374 is mainly recommended for the extrusion of very thin film for light duty applications. It contains both slip additives (target 600 ppm erucamide) and anti blocking additives (target 900 ppm) as well as antioxidants.
Lotrene® FD0374 LDPE TDS
POLYMER PROPERTIES | VALUE | UNIT | TEST METHOD |
Melt Flow Index | 3.5 | g/10 min. | ASTM D1238- |
Density @ 23 °C | 0.923 | g/cm3 | ASTM D1505- |
Crystalline Melting Point | 108 | °C | ASTM E794- |
Vicat Softening Point | 89 | °C | ASTM D1525- |
FILM PROPERTIES | VALUE | UNIT | TEST METHOD |
Tensile Strength @ Yield MD/ TD | 11/11 | MPa | ASTM D882- |
Tensile Strength @ Break MD/ TD | 25/22 | MPa | ASTM D882- |
Elongation @ Break MD/ TD | 320/600 | % | ASTM D882- |
Impact Strength, F 50 | 100 | g | ASTM D1709- |
Tear resistance MD/ TD | 65/35 | N/mm | ASTM D- 1922 |
| 0.11 | | ASTM D1894 |
Haze | 8 | % | ASTM D1003- |
Gloss @ °45 | 56 | - | ASTM D2457- |
Lotrène FD0474 is mainly recommended for the extrusion of very high clarity blown and cast films, It contains both slip additives (target 600 ppm erucamide) and anti blocking additives (target 900 ppm) as well as antioxidants.
Lotrene® FD0474 LDPE TDS
POLYMER PROPERTIES | VALUE | UNIT | TEST METHOD |
Melt Flow Index | 4.0 | g/10 min. | ASTM D1238- |
Density @ 23 °C | 0.923 | g/cm3 | ASTM D1505- |
Crystalline Melting Point | 108 | °C | ASTM E794- |
Vicat Softening Point | 87 | °C | ASTM D1525- |
FILM PROPERTIES | VALUE | UNIT | TEST METHOD |
Tensile Strength @ Yield MD/ TD | 11/11 | MPa | ASTM D882- |
Tensile Strength @ Break MD/ TD | 23/20 | MPa | ASTM D882- |
Elongation @ Break MD/ TD | 335/610 | % | ASTM D882- |
Impact Strength, F 50 | 90 | g | ASTM D1709- |
Tear resistance MD/ TD | 75/40 | N/mm | ASTM D- 1922 |
| 0.09 | | ASTM D1894 |
Haze | 7 | % | ASTM D1003- |
Gloss @ °45 | 63 | - | ASTM D2457- |
Lotrène FE3000 is an additive free grade produced by a tubular high pressure process mainly recommended for heavy duty film applications.
Lotrene® FE3000 LDPE TDS
POLYMER PROPERTIES | VALUE | UNIT | TEST METHOD |
Melt Flow Index | 0.30 | g/10 min. | ASTM D1238- |
Density @ 23 °C | 0.923 | g/cm3 | ASTM D792- |
Crystalline Melting Point | 112 | °C | ASTM E794- |
Vicat Softening Point | 99 | °C | ASTM D1525- |
FILM PROPERTIES | VALUE | UNIT | TEST METHOD |
Tensile Strength @ Yield MD/ TD | 12/12 | MPa | ASTM D882- |
Tensile Strength @ Break MD/ TD | 35/29 | MPa | ASTM D882- |
Elongation @ Break MD/ TD | 400/600 | % | ASTM D882- |
Impact Strength, F 50 | 150 | g | ASTM D1709- |
Tear resistance MD/ TD | 47/47 | N/mm | ASTM D1922- |
Puncture Force | 62 | N | Internal Method |
| 0.75 | | ASTM D1894- |
Haze | 8 | % | ASTM D1003- |
Gloss (@ 45 ) | 56 | | ASTM D2457- |
Lotrène FE8000 is an additive free grade, produced by a high pressure tubular process, mainly recommended for light and medium duty film applications with good optical properties and medium rigidity.
Lotrene® FE8000 LDPE TDS
POLYMER PROPERTIES | VALUE | UNIT | TEST METHOD |
Melt Flow Index | 0.80 | g/10 min. | ASTM D1238- |
Density @ 23 °C | 0.923 | g/cm3 | ASTM D792- |
Crystalline Melting Point | 111 | °C | ASTM E794- |
Vicat Softening Point | 97 | °C | ASTM D1525- |
FILM PROPERTIES | VALUE | UNIT | TEST METHOD |
Tensile Strength @ Yield MD/ TD | 12/12 | MPa | ASTM D882- |
Tensile Strength @ Break MD/ TD | 34/27 | MPa | ASTM D882- |
Elongation @ Break MD/ TD | 410/615 | % | ASTM D882- |
Impact Strength, F 50 | 115 | g | ASTM D1709- |
Tear resistance MD/ TD | 70/40 | N/mm | ASTM D- 1922 |
Puncture Force | 51 | N | Internal Method |
| 0.9 | - | ASTM D1894- |
Haze | 7 | % | ASTM D1003- |
Gloss (@ 45 °) | 61 | - | ASTM D2457- |
Lotrène FE8004 is produced by a high pressure tubular process and is mainly recommended for light and medium duty film applications with good optical properties. It contains slip agent (target: 300 ppm erucamide).
Lotrene® FE8004 LDPE TDS
POLYMER PROPERTIES | VALUE | UNIT | TEST METHOD |
Melt Flow Index | 0.80 | g/10 min. | ASTM D1238- |
Density @ 23 °C | 0.923 | g/cm3 | ASTM D792- |
Crystalline Melting Point | 111 | °C | ASTM E794- |
Vicat Softening Point | 97 | °C | ASTM D1525- |
FILM PROPERTIES | VALUE | UNIT | TEST METHOD |
Tensile Strength @ Yield MD/ TD | 12/12 | MPa | ASTM D882- |
Tensile Strength @ Break MD/ TD | 34/28 | MPa | ASTM D882- |
Elongation @ Break MD/ TD | 390/630 | % | ASTM D882- |
Impact Strength, F 50 | 110 | g | ASTM D1709- |
Tear resistance MD/ TD | 75/40 | N/mm | ASTM D- 1922 |
Puncture Force | 38 | N | Internal Method |
| 0.2 | | ASTM D1894- |
Haze | 7 | % | ASTM D1003- |
Gloss (@ 45 °) | 62 | | ASTM D2457- |