Marlex C513UV HDPE

Home » Marlex C513UV

Typical blow molded applications:

NOMINAL PHYSICAL PROPERTIES	English	SI
Density	—	0.945 g/cm3
Flow Rate (HLMI, 190 °C/21.6 kg)	—	6.2 g/10 min
Tensile Strength at Yield, 2 in/min, Type IV bar	3,500 psi	24 MPa
Elongation at Break, 2 in/min, Type IV bar	700 %	700 %
Flexural Modulus, Tangent – 16:1 span:depth, 0.5 in/min	155,000 psi	1070 MPa
ESCR, Condition A (100% Igepal), F50	> 2000 h	> 2000 h
ESCR, Condition B (100% Igepal), F50	> 2000 h	> 2000 h
Durometer Hardness, Type D (Shore D)	61	61
Vicat Softening Temperature, Loading 1, Rate A	254 °F	123 °C
Heat Deflection Temperature, 66 psi, Method A	150 °F	66 °C
Brittleness Temperature, Type A, Type I specimen	< -103 °F	< -75 °C
Tensile Impact, Type S bar	275 ft-lb/in2	580 kJ/m2

Marlex C513UV