Marlex HXM50100

Marlex HXM50100 HDPE

Marlex HXM50100 HDPE

Typical blow molded applications:

  • Shippingcontainers
  • Jerrycans
  • Fuelcontainers
  • Agriculturalchemical tanks

Typical thermoformed applications:

  • Pallets
  • Automotivedunnage
  • Truckbedliners
  • Playgroundequipment
Density0.948 g/cm3
Flow Rate (HLMI, 190 °C/21.6 kg)10.0 g/10 min
Tensile Strength at Yield, 2 in/min, Type IV bar3,600 psi25 MPa
Elongation at Break, 2 in/min, Type IV bar700 %700 %
Flexural Modulus, Tangent – 16:1 span:depth, 0.5 in/min175,000 psi1,200 MPa
ESCR, Condition B (100 % Igepal), F50> 1,000 h> 1,000 h
Durometer Hardness, Type D (Shore D)6868
Vicat Softening Temperature, Loading 1, Rate A258 °F126 °C
Heat Deflection Temperature, 66 psi, Method A173 °F78 °C
Brittleness Temperature, Type A, Type I specimen< -103 °F< -75 °C
Tensile Impact, Type S bar90 ft•lb/in2190 kJ/m2